1. Properties of TiO2 thin films deposited by rf reactive magnetron sputtering on biased substrates.
- Author
-
Nezar, Sawsen, Saoula, Nadia, Sali, Samira, Faiz, Mohammed, Mekki, Mogtaba, Laoufi, Nadia Aïcha, and Tabet, Nouar
- Subjects
- *
TITANIUM dioxide films , *MAGNETRON sputtering , *SUBSTRATES (Materials science) , *X-ray diffraction , *FOURIER transform infrared spectroscopy - Abstract
TiO 2 thin films are of paramount importance due to their pervasive applications. In contrast to previous published works where the substrate was heated at high temperatures to obtain TiO 2 crystalline phase, we show in this study that it is possible to deposit crystalline TiO 2 thin films on biased and unbiased substrate at room temperature using reactive rf magnetron sputtering. The bias voltage was varied from 0 V to −100 V. The deposited films were characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), UV–vis spectroscopy, Raman spectroscopy, X-ray Photoelectron Spectroscopy (XPS) and atomic force microscopy (AFM). The average crystallite size was estimated using x-ray diffraction. The results showed that the application of negative bias affects the surface roughness of the films and favors the formation of the rutile phase. The root mean square roughness (R rms ), the average grain size and the optical band gap of the films decreased as the substrate bias voltage was varied from 0 to −100 V. The UV–visible transmittance spectra showed that the films were transparent in the visible range and absorb strongly in the UV range. This study shows that biasing the substrate could be a promising and effective alternative to deposit TiO 2 crystallized thin films of engineered properties at room temperature. [ABSTRACT FROM AUTHOR]
- Published
- 2017
- Full Text
- View/download PDF