Well-defined polarization-electric field double hysteresis loops are rarely observed in pure NaNbO3 (NN) ceramics due to the metastability of the field-induced ferroelectric phase. In order to stabilize the antiferroelectric phase, various ABO3-type binary oxides were incorporated into a NaNbO3 ceramic, where the B-site is occupied with transition elements. In this work, CaSnO3 was chosen to construct the NaNbO3-based solid solution by reducing the Goldschmidt tolerance factor and ionic polarizability. X-ray diffraction patterns, transmission electron microscopy images, and Raman spectra indicate enhanced antiferroelectricity. Typical double hysteresis loops were also observed from polarization-electric field measurements in ambient conditions with slightly weakened maximum polarization as the content of CaSnO3 increased. Our results reveal the generality of this strategy and pave the way for various applications involving high-power energy for NaNbO3-based ceramics. [ABSTRACT FROM AUTHOR]

The pulsed power supply that generates megawatts of electrical power has drawn important attention for many decades. Despite that the large energy output has been obtained in lead-containing materials such as Pb(Zr0.95Ti0.05)O3 (PZT95/5) ceramics, lead-free ferroelectric candidates are highly desired due to the environmental concerns. In this work, we report the depolarization behavior of lead-free ternary 0.99[0.98(Bi0.5Na0.5)(Ti0.995Mn0.005)O3-0.02BiAlO3]-0.01NaNbO3 ferroelectric ceramics under shock wave compression. A current profile with a maximum value of ∼25 A and a FWHM of ∼2.3 μs was obtained. Particularly, the poled BNT-BA-0.01NN ceramics were almost completely depolarized under high strain rate loading, releasing a high charge density J of 38 μC/cm2. The released J was approximately 96% of thermal-induced charge density (∼40 μC/cm2), which was 18% higher than that of PZT95/5 ceramics. The shock-induced depolarization mechanism can be attributed to the ferroelectric-ergodic relaxor phase transition. These results reveal the BNT-based ceramics as promising candidates for pulsed power applications. [ABSTRACT FROM AUTHOR]