Well-defined polarization-electric field double hysteresis loops are rarely observed in pure NaNbO3 (NN) ceramics due to the metastability of the field-induced ferroelectric phase. In order to stabilize the antiferroelectric phase, various ABO3-type binary oxides were incorporated into a NaNbO3 ceramic, where the B-site is occupied with transition elements. In this work, CaSnO3 was chosen to construct the NaNbO3-based solid solution by reducing the Goldschmidt tolerance factor and ionic polarizability. X-ray diffraction patterns, transmission electron microscopy images, and Raman spectra indicate enhanced antiferroelectricity. Typical double hysteresis loops were also observed from polarization-electric field measurements in ambient conditions with slightly weakened maximum polarization as the content of CaSnO3 increased. Our results reveal the generality of this strategy and pave the way for various applications involving high-power energy for NaNbO3-based ceramics. [ABSTRACT FROM AUTHOR]

(Pb0.325Sr0.675)TiO3 (PST) ceramics were prepared by a traditional solid-state reaction technique. The dielectric and enhanced pyroelectric properties of PST ceramics were investigated under a DC bias field. The dielectric permittivity and dielectric loss of PST ceramics at Curie temperature were 2.97 × 10-4 and 0.006 without DC bias field, respectively. With a DC electric field of 0-500 V/mm, the maximum pyroelectric coefficient and the largest figure of merit (Fd) of PST ceramics were obtained, about 60 × 10-8 C cm-2 K-1 and 26 × 10-5 Pa-1/2, respectively. PST ceramics with such superior electric field enhanced pyroelectric properties have the potential for uncooled focal plane array detectors application. [ABSTRACT FROM AUTHOR]