Search

A study of the structural characteristics of the composites [Pb(Fe0.5Nb0.5)O3(PFN)] x -[Cr0.75Fe1.25O3(CRFO)]100− x ( x = 0 (CRFO100), 10, 50, 90, 100) was performed in this work. The compounds PFN100 and CRFO100 were prepared by conventional solid-state method and investigated by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), and 57Fe Mössbauer Spectroscopy techniques. The X-ray analysis shows that PFN100 is tetragonal and the CRFO100 phase has a trigonal symmetry. The refinement of all the composites was also performed and discussed in this paper. The Mössbauer spectrum for the composite samples shows a paramagnetic doublet and a sextet probably assigned to a magnetic phase associated to Fe+3. For the sample PFN100, only a magnetic field of 49.5 T (isomer shift (δ) = 0.21 mm/s) was detected. For the composite sample, the δ and Δ are typical of Fe ions at sites of octahedral coordination. [ABSTRACT FROM AUTHOR]

Gd3+ was chosen as a substitute for Bi3+ in BiNbO4 ceramics, and the substitution effects on the sintering performance and microwave dielectric properties were studied in this paper. The high temperature triclinic phase was observed only in the Bi0.98Gd0.02NbO4 ceramics when sintered at 920 °C. Both bulk densities and dielectric constant (εr) increased with the sintering temperature, while decreased with the Gd content. The quality factor ( Q) exhibited a correlation to the Gd content and the microstructures of Bi1− x Gd x NbO4 ceramics. At the sintering temperature of 900 °C, Bi0.992Gd0.008NbO4 ceramics exhibited microwave dielectric properties of εr ∼ 43.87, Q × f ∼ 16,852 GHz (at 4.3 GHz), and its temperature coefficient of resonant frequency (τf) was found to be near-to-zero. [ABSTRACT FROM AUTHOR]

A significant weight loss of copper plate was observed after copper-water vapor interaction near critical point. This leads to the acceleration of the ceramic layer formation on SUS surface during granite-water vapor interaction in the presence of copper. In this paper, we have determined the chemical state of copper at which the mass transfer takes place through reaction with H2 and O2+N2 gas mixture at the different O2 amount. Obtained results indicate that the weight loss of copper plate occurs at Cu2O (+1) state due to a complex processes. The morphology of copper species on the surface of mesh and granite suggests that the Cu2O was dissolved in water vapor and recrystallized on the surface of mesh and granite. Copper species were characterized by X-ray diffraction(XRD), scanning electron microscopy (SEM) equipped with an energy dispersive X-ray (EDX). [ABSTRACT FROM AUTHOR]

Solid oxide fuel cells are currently constructed using a yttria stabilised zirconia electrolyte membrane. However, zirconia has a number of disadvantages associated with its use, such as the high operational temperatures required for it to exhibit acceptable levels of ionic conductivity. Alternative ceramics such as doped cerium oxide show promise as electrolytes capable of operating at reduced temperatures, but introduce additional problems such as electronic conduction and inferior mechanical properties. This paper describes the manufacture and characterisation of a number of prototype electrolytes consisting of a mixture of yttria stabilised zirconia and gadolinium doped ceria. Traditional ceramic processing techniques were used to produce the samples, which were then examined using dilatometry, impedance spectroscopy and X-ray diffraction. Results show a lowering of the ionic conductivity of zirconia with the addition of doped ceria. X-ray diffraction patterns obtained from the samples suggested that this effect could be attributed to the formation of a solid solution of ceria in zirconia. [ABSTRACT FROM AUTHOR]